CRY 18

CRY 18
CRY-018 is the mixed rare-earth silicate single crystal scintillation material

Key characteristics

  • medium density
  • high light yield
  • short decay time

Technical parameters

 

 Physical properties
  CRY 18 YAG:Ce YAP:Ce LuAG:Ce LuAG:Pr LuAP:Ce BGO PWO CRY 19
Density  4.5 g/cm3 4.57 g/cm3  5.37 g/cm3  6.73 g/cm3  6.73 g/cm3  8.34 g/cm3  7.13 g/cm3  8.28 g/cm3  7.1 g/cm3
Hardness by Mohs  5.8 8.5  8.6  8.5  8.5  -  5  4  -
Index of refraction  1.79 1.82  1.95  1.84  1.84  -  2.15  2.17  1.81
Melting point  1980°C 1970°C  1875°C  2020°C  2043°C  1960 °C  1050 °C  1123 °C  2100°C
Thermal expansion  - 0.8-0.9 x 10-5/K  0.4-1.1 x 10-5/K  -  -  -  0.7 x 10-5/K  -  1.8-10.3 x 10-5/K
Crystal structure  monoclinic cubic  rhombic  cubic  cubic  -  cubic  tetragonal symetric  monoclinic
Hygroscopic  NO NO  NO  NO  NO  NO  NO  NO  NO
Scintillation properties
Wavelength of max. emission  425 nm 550 nm  370 nm  535 nm  310 nm  365 nm  480 nm  420 nm  420 nm
Decay constant  45 ns 70 ns  25 ns  70 ns  20 ns  18 ns  300 ns  5-15 ns  41 ns
Afterglow  - <0.005 % at 6 ms  <0.005 % at 6 ms  -  -  -  <0.005% at 6 ms  -  -
Radiation length for 511 keV  2.74 cm 3.5 cm  2.7 cm  1.3 cm  1.3 cm  -  1.1 cm  0.89 cm  2.1 cm
Photon yield at 300 K (27°C)  30 x 103 Ph/MeV 30 x 103 Ph/MeV  25 x 103 Ph/MeV  25 x 103 Ph/MeV  15-18 x 103 Ph/MeV  11 x 103 Ph/MeV  8-10 x 103 Ph/MeV  15-25 phe/MeV  24 x 103 Ph/MeV
Integrated light output compared to NaI:Tl  80 % NaI:Tl 40 % NaI:Tl  70 % NaI:Tl  20 % NaI:Tl  66 % NaI:Tl  -  15-20 % NaI:Tl  -  75 % NaI:Tl