LuAP :Ce

LuAP :Ce
Lutetium aluminium perovskite doped with cerium

Technical parameters

 

 Physical properties
  LuAP:Ce YAG:Ce YAP:Ce LuAG:Ce CRY 18 LuAG:Pr BGO PWO CRY 19
Density  8.34 g/cm3 4.57 g/cm3  5.37 g/cm3  6.73 g/cm3  4.5 g/cm3  6.73 g/cm3  7.13 g/cm3  8.28 g/cm3  7.1 g/cm3
Hardness by Mohs  - 8.5  8.6  8.5  5.8  8.5  5  4  -
Index of refraction  - 1.82  1.95  1.84  1.79  1.84  2.15  2.17  1.81
Melting point  1960 °C 1970°C  1875°C  2020°C  1980°C  2043°C  1050 °C  1123 °C  2100°C
Thermal expansion  - 0.8-0.9 x 10-5/K  0.4-1.1 x 10-5/K  -  -  -  0.7 x 10-5/K  -  1.8-10.3 x 10-5/K
Crystal structure  - cubic  rhombic  cubic  monoclinic  cubic  cubic  tetragonal symetric  monoclinic
Hygroscopic  NO NO  NO  NO  NO  NO  NO  NO  NO
Scintillation properties
Wavelength of max. emission  365 nm 550 nm  370 nm  535 nm  425 nm  310 nm  480 nm  420 nm  420 nm
Decay constant  18 ns 70 ns  25 ns  70 ns  45 ns  20 ns  300 ns  5-15 ns  41 ns
Afterglow  - <0.005 % at 6 ms  <0.005 % at 6 ms  -  -  -  <0.005% at 6 ms  -  -
Radiation length for 511 keV  - 3.5 cm  2.7 cm  1.3 cm  2.74 cm  1.3 cm  1.1 cm  0.89 cm  2.1 cm
Photon yield at 300 K (27°C)  11 x 103 Ph/MeV 30 x 103 Ph/MeV  25 x 103 Ph/MeV  25 x 103 Ph/MeV  30 x 103 Ph/MeV  15-18 x 103 Ph/MeV  8-10 x 103 Ph/MeV  15-25 phe/MeV  24 x 103 Ph/MeV
Integrated light output compared to NaI:Tl  - 40 % NaI:Tl  70 % NaI:Tl  20 % NaI:Tl  80 % NaI:Tl  66 % NaI:Tl  15-20 % NaI:Tl  -  75 % NaI:Tl
Energy resolution at 662 keV  11.5 %  -  -  -  -  -  -  -  -